Designed by System Three® as moisture barrier coatings, Clear Coat Kits are easy to apply, with no hazardous solvents. These coatings are especially useful in construction where constant immersion is likely, as in boats. The mixed epoxy is applied with a roller, or a brush, without thinning. Each coat is allowed to cure before recoating, and recoating can be done without sanding, if done within three days. For continued exposure to sunlight, a spar varnish coating over the moisture barrier coating is recommended for UV protection.
Features:
- Clear, almost water-white, solvent-free epoxy system
- Cures to a durable, clear, glossy, blush-free surface
- Convenient 2:1 mixing ratio
- Moisture barrier coatings
- Especially useful in construction where constant immersion is likely, as in boats.
Specifications:
- Type: 2-component, low viscosity, 100% solids epoxy system
- Size: 12 oz
- Sheen: Satin
- Color: Clear
- Mix Ratio by Weight (resin to hardener): 100/43
- Mix ratio by Volume (resin to hardener): 100/50 or 2:1
- Total Solids: 100%
- Mixed Viscosity: 380 CPS
- Tensile Strength (PSI): 7,800
- Tensile Elongation at Break: 8%
- Flexural Strength (PSI): 12,000
- Flexural Modulus (PSI): 375,000
- Compressive Strength (PSI): Yield 13,000 - Failure: 26,000
- Recommended Use: Directed at, but not limited to, the coating and laminating of fiber composites and wood
- Application Method: brush or roll on
- Coverage: approximately 50 sq.ft. with a 3 mil coverage
- Minimum Application Temperature: 50°F
- Optimal Application Temperature: 77°F
- Working Time at 77°F: 60 minutes
- Gel Time at 77°F: 60 minutes (100g mixutre)
- Tack FreeTime Thin Film at 77°F: 24 hours
- Full Cure at 77°F: 72 hours
- Material VOC (g/L): None
What's Included:
- (1) Clear Coat Epoxy - Part A - 8 fl.oz.
- (1) Clear Coat Hardener - Part B - 4 fl.oz.